3M™ Scotch-Weld™ Toughened Epoxy Adhesive LSB60NS, Gray, 400 mL Duo-Pak, 6/case

257992 MFG #: 051115-63426
$90.76 / EACH
  • Application Time: 90, 90 min
  • Base Type: Epoxy
  • Brand: Scotch-Weld™
  • Color: Part A: White/Part B: Black
  • Container Size: 400, 400 mL
  • Container Type: Dual Cartridge, Dual-Cartridge
  • Curing Time: 7 Days at 72 deg F
  • Flammability Rating: 1
  • Flash Point: Part A: >/=240 deg F/Part B: >250 deg F
  • For Use On: Ceramic, Glass, Hardboard, Metal and Wood
  • Form: Part A: Viscous /Part B: Paste
  • Functional Cure: 10
  • Mixing Ratio: 0.042361111, 0.0423611111111111, 0.042361111111111106, 1:1
  • Net Weight: Base: 10.1 lb/gal/Accelerator: 9.8 lb/gal
  • Odor/Scent: Epoxy
  • Setting Time: 10, 10 hr
  • Shear Strength: 4500, 4500 psi
  • Specific Gravity: Part A: 1.17/Part B: 1.21
  • Temperature Range: 72
  • Temperature Rating: 72, 72 deg F
  • Type: 2-Part
  • Viscosity Rating: Part A: 90000 to 100000 cPs/Part B: 24000 to 25000 cPs
  • VOC Content: <1, <1 g/L
  • Work Life: 90

When using a Duo-Pak (DP) size adhesive, rely on 3M dispensing equipment for convenient and accurate metering, mixing and dispensing.

3M™ Scotch-Weld™ Toughened Epoxy Adhesive LSB60NS
Used in large structure bonding for aluminum honeycomb panels
Works Efficiently for Large Structure Bonding
Unlike using screws or rivets, 3M™ Scotch-Weld™ Toughened Epoxy Adhesive LSB60NS lets you distribute stress uniformly over the entire bonded area while maintaining surface integrity and the physical properties of the panel. It allows you to use thinner, lighter panel materials without worrying about distortion, splitting, or crazing and will secure even small or thin bonding edges. Offering high resistance against shock and vibration, it features good shear and peel adhesion with high levels of durability.

Recommended Applications
  • Delivery truck side walls
  • Metal enclosure facing and cabinets
  • Panels to frame
90 Minute Work Life Provides Ample Time for Positioning and Adjustment
This epoxy dispenses as a medium viscosity adhesive for easy, controlled dispensing. The adhesive reaches handling strength in approximately 6 hours and is fully cured in 7 days at 73°F (23°C).The mix ratio is 1:1 and provides a 90 minute work life, providing ample time to adjust for desired fit prior to curing. 3M™ Scotch-Weld™ Toughened Epoxy Adhesive LSB60NS is ideal for bulk application through meter mix dispensing equipment and the manufacture of large panel products.

Understanding Epoxy Adhesives
Epoxy adhesives are part of the class of adhesives called "structural adhesives," which also includes polyurethane, acrylic, cyanoacrylate and others. Epoxies are formulated as liquid reactive polymers that undergo a chemical reaction when mixed and then cure to form a solid plastic material. Once the two parts are mixed in their specified ratio, they begin the curing process and offer a limited working time where the adhesive can be applied and the two surfaces positioned as needed. This work life lasts anywhere from a few minutes to several hours. These structural adhesives provide high shear and peel strengths, depending on the formula, and better heat and chemical resistance than other common adhesives. In general, epoxy adhesives have the highest overall strength and offer the best performance and most resistance to high temperatures, solvents and outdoor weathering.

Epoxy adhesives are widely used in building and home construction; aircraft and automobile manufacturing; bicycle, boat, golf clubs, ski and snowboard assembly as well as a host of home use and other applications. They are used virtually anywhere high-strength bonds are needed along with resistance to environmental conditions. These ad
QTY
  • Features
  • 90 min worklife provides ample time for positioning and adjustment
  • Features good long term holding power and high peel strength
  • Delivers non-sag formulation so adhesive stays where applied
  • Ideal for bulk application through meter mix dispensing equipment
  • High performance, 2-part, toughened epoxy adhesives offering outstanding shear adhesion and very high levels of durability with a choice of flow characteristics
  • 1:1 mix ratio for easy automated large volume dispensing
  • OSHA 29 CFR 1910.1200